Avery Dennison
MED 6651R
Double-Coated Foam
MED 6651R is a double-coated, white, soft, conformable, thin, closed-cell polyolefin foam with a synthetic rubber adhesive. This product offers a good initial tack, allowing for adhesion to various natural and synthetic substrates. It contains a heavy-weight liner with ideal release for kiss cutting, die cutting and converting.
Typical Application
Designed for ostomy application and fixation devices.
Features and Benefits
- Thin and conformable
- Moisture resistant
- Die cuttable
- Gamma and EtO sterilizable
|
Physical Properties (Not intended as a specification.)
|
Test Method**
|
Typical Values*
|
|---|---|---|
|
Peel Adhesion on Polyethylene (PE) - Liner
|
TDS-02
|
6.0 N/25 mm
|
|
Peel Adhesion on Polyethylene (PE) - Unwind
|
TDS-02
|
6.0 N/25 mm
|
|
Peel Adhesion on Stainless Steel (SS) - Liner
|
TDS-04
|
39.0 N/25 mm
|
|
Peel Adhesion on Stainless Steel (SS) - Unwind
|
TDS-04
|
42.0 N/25 mm
|
|
Liner Release
|
TDS-06
|
30 g/25 mm
|
|
Finat Tack - Liner
|
TDS-08
|
4 N/25 mm
|
|
Finat Tack - Unwind
|
TDS-08
|
5 N/25 mm
|
|
Static Shear - Liner
|
TDS-13
|
>11,000 minutes
|
|
Static Shear - Unwind
|
TDS-13
|
>11,000 minutes
|
|
Elongation Machine Direction
|
TDS-15
|
400%
|
|
Elongation Cross Direction
|
TDS-15
|
375%
|
|
Load at Break Machine Direction
|
TDS-15
|
8 lbf/in 35 N/ 25mm
|
|
Load at Break Cross Direction
|
TDS-15
|
5 lbf/in 20 N/ 25mm
|
|
Product Construction
|
Typical Values*
|
Description
|
|---|---|---|
|
Unwind Adhesive Thickness
|
1.6 mils 40 µm
|
Solventless acrylic adhesive designed for medical applications
|
|
Carrier Thickness
|
31.5 mils 800 µm
|
White, crosslinked, closed cell polyolefin foam
|
|
Liner Adhesive Thickness
|
1.6 mils 40 µm
|
Synthetic rubber adhesive designed for medical applications
|
|
Release Liner Thickness
|
3.2 mils 80 µm
|
Blue/green super-calendered glassine
|
*Refer to product specifications for material acceptance limits. **Test method information available upon request.
STORAGE AND SHELF LIFE
Two years when stored at 23°C (73°F), 50% relative humidity, out of direct sunlight, in original packaging.